Glass
Transition Temperature (°C) |
90 |
|
Crystalline
Melting Point (°C) |
N/A |
Room
Temperature Density (kg/m^3) |
1070 |
Maximum
Operating Temperature (°C) |
55 |
Process
Range (°C) |
22 - 270 |
No
Flow Temperature (°C) |
140 |
Average
Specific Heat Capacity (J/kg °K) |
1870 |
Average
Thermal Diffusivity (mm^2/s) |
0.08 |
Vicat
Softening Point (°C) |
105 |
HDT
(0.45 MPa) (°C) |
96 |
HDT
(1.80 MPa) (°C) |
84 |
Chain
Structure: Amorphous
|
Tensile
Strength (MPa) |
72 |
Elongation
@ break (%) |
2 |
|
Impact
Strength (kJ/m) |
0.020 |
Flexural
Modulus (GPa) |
3.60 |
Flammability
Rating (UL94) |
HB |
Drying
Time (Hrs) |
2 |
Drying
Temperature (°C) |
70 |
©
SkidMark Multimedia Productions MMIV..
|
|
|