NOTE: These values are representative values and do not relate to a specific grade of material
Generic Type: POLY STYRENE S.I. Abbr: PS
Glass Transition Temperature (°C) 90
Crystalline Melting Point (°C) N/A
Room Temperature Density (kg/m^3) 1080
Maximum Operating Temperature (°C) 50
Process Range (°C) 200 - 250
No Flow Temperature (°C) 130
Average Specific Heat Capacity (J/kg °K) 1820
Average Thermal Diffusivity (mm^2/s) 0.08
Vicat Softening Point (°C) 105
HDT (0.45 MPa) (°C) 85
HDT (1.80 MPa) (°C) 75
Chain Structure: Amorphous
Tensile Strength (MPa) 42
Elongation @ break (%) 3
Shear Viscosity Vs Shear Rate PVT Specific Volume as a function of Pressure, Temperature Specific Heat Capacity as a function of Temperature Thermal Diffusivity as a function of Temperature
Applications
Graphical Information
Impact Strength (kJ/m) 0.100
Flexural Modulus (GPa) 2.10
Flammability Rating (UL94) HB
Drying Time (Hrs) 2
Drying Temperature (°C) 70
© SkidMark Multimedia Productions MMIV..
Reproduced by kind permission of SkidMark Multimedia Productions. NEXUS III is a product of SkidMark Multimedia Productions. © 2004