Glass
Transition Temperature (°C) |
-10 |
|
Crystalline
Melting Point (°C) |
160 |
Room
Temperature Density (kg/m^3) |
905 |
Maximum
Operating Temperature (°C) |
100 |
Process
Range (°C) |
210
- 290 |
No
Flow Temperature (°C) |
150 |
Average
Specific Heat Capacity (J/kg °K) |
2900 |
Average
Thermal Diffusivity (mm^2/s) |
0.08 |
Vicat
Softening Point (°C) |
130 |
HDT
(0.45 MPa) (°C) |
105 |
HDT
(1.80 MPa) (°C) |
65 |
Chain
Structure: Semi-Crystalline
|
Tensile
Strength (MPa) |
33 |
Elongation
@ break (%) |
150 |
|
Impact
Strength (kJ/m) |
0.070 |
Flexural
Modulus (GPa) |
1.50 |
Flammability
Rating (UL94) |
HB |
Drying
Time (Hrs) |
N/A |
Drying
Temperature (°C) |
N/A |
©