Glass
Transition Temperature (°C) |
114 |
|
Crystalline
Melting Point (°C) |
335 |
Room
Temperature Density (kg/m^3) |
1300 |
Maximum
Operating Temperature (°C) |
250 |
Process
Range (°C) |
350
- 390 |
No
Flow Temperature (°C) |
350 |
Average
Specific Heat Capacity (J/kg °K) |
2000 |
Average
Thermal Diffusivity (mm^2/s) |
0.15 |
Vicat
Softening Point (°C) |
260+ |
HDT
(0.45 MPa) (°C) |
260+ |
HDT
(1.80 MPa) (°C) |
160 |
Chain
Structure: Semi-Crystalline
|
Tensile
Strength (MPa) |
91 |
Elongation
@ break (%) |
50 |
|
Impact
Strength (kJ/m) |
0.085 |
Flexural
Modulus (GPa) |
3.80 |
Flammability
Rating (UL94) |
V0 |
Drying
Time (Hrs) |
3 |
Drying
Temperature (°C) |
150 |
©
SkidMark Multimedia Productions MMIV..
|
|
|