IIR
- Butyl Rubber |
Glass
Transition Temperature (°C) |
-66 |
Room
Temperature Density (kg/m^3) |
992 |
Maximum
Working Temperature (°C) |
150 |
Tensile
Strength (MPa) |
M |
Resistance
To Tear |
M/H |
Resistance
To Abrasion |
M |
Compression
set @ -20°C (%) |
12 |
Compression
set @ +23°C (%) |
18 |
Compression
set @ +120°C (%) |
60 |
Swelling
/ 70Hr / ASTM Oil No.3 @ 70°C (%) |
>140 |
Swelling
/ 70Hr / Fuel C @ Room Temperature (%) |
--- |
Gas
Permeability |
VL |
Ozone
Resistance |
M |
Oxidation
Resistance |
VH |
Rebound
(Hot) |
H |
Rebound
(Cold) |
VL |
Heat Resistance
5 Hours (°C) |
200 |
Heat Resistance
70 Hours (°C) |
160 |
Heat Resistance
1000 Hours (°C) |
130 |
|
|