| CR
- Polychloroprene Rubber |
| Glass
Transition Temperature (°C) |
-45 |
| Room
Temperature Density (kg/m^3) |
1233 |
| Maximum
Working Temperature (°C) |
125 |
| Tensile
Strength (MPa) |
H |
| Resistance
To Tear |
H |
| Resistance
To Abrasion |
M/H |
| Compression
set @ -20°C (%) |
50 |
| Compression
set @ +23°C (%) |
10 |
| Compression
set @ +120°C (%) |
30 |
| Swelling
/ 70Hr / ASTM Oil No.3 @ 100°C (%) |
80 |
| Swelling
/ 70Hr / Fuel C @ Room Temperature (%) |
--- |
| Gas
Permeability |
L |
| Ozone
Resistance |
M |
| Oxidation
Resistance |
VH |
| Rebound
(Hot) |
VH |
| Rebound
(Cold) |
VH |
| Heat Resistance
5 Hours (°C) |
180 |
| Heat Resistance
70 Hours (°C) |
130 |
| Heat Resistance
1000 Hours (°C) |
100 |
|
|
|