AU
- Polyester Urethane Rubber |
Glass
Transition Temperature (°C) |
-35 |
Room
Temperature Density (kg/m^3) |
1033
<>
1243 |
Maximum
Working Temperature (°C) |
75 |
Tensile
Strength (MPa) |
H |
Resistance
To Tear |
H |
Resistance
To Abrasion |
H |
Compression
set @ -20°C (%) |
25 |
Compression
set @ +23°C (%) |
7 |
Compression
set @ +120°C (%) |
70 |
Swelling
/ 70Hr / ASTM Oil No.3 @ 100°C (%) |
40 |
Swelling
/ 70Hr / Fuel C @ Room Temperature (%) |
--- |
Gas
Permeability |
--- |
Ozone
Resistance |
H |
Oxidation
Resistance |
--- |
Rebound
(Hot) |
--- |
Rebound
(Cold) |
--- |
Heat Resistance
5 Hours (°C) |
170 |
Heat Resistance
70 Hours (°C) |
100 |
Heat Resistance
1000 Hours (°C) |
75 |
|
|